雾化合金粉末系列
发布日期：2020-04-15 13:57:02 浏览次数：
雾化合金粉是指用雾化法制得的金属粉末，即利用高压气流或水流、离心力等工艺，将一种或多种熔融金属液流粉碎成液滴，冷凝后得到的金属或合金粉末。根据雾化介质的不同，雾化法可以分为气雾化、水雾化、离心雾化等工艺。气雾化粉末球形度好，杂质含量低；水雾化粉末形貌属于不规则形状，含氧量高，粉末成型保型性好。公司雾化合金粉系列ag真人国际官网主要有雾化合金粉-316L、304L(奥氏体不锈钢合金粉)、雾化合金粉-17-4PH(马氏体不锈钢合金粉)、雾化合金粉-F75(钴铬钼高温合金粉)。
雾化粉末特性:
- 纯度高，杂质含量少;
- 粉末表面光滑;
- 烧结ag真人国际官网机械性能好.
1、水气联合雾化
| 牌号 |
成分 (Wt%) |
D50 |
| Cr |
Ni |
Mo |
Cu |
Mn |
Si |
C |
O |
Other |
| 316L |
16-18 |
10-14 |
2-3 |
|
≤2 |
≤1 |
≤0.03 |
≤0.4 |
|
8-13 |
| 17-4PH |
15.5-17.5 |
3-5 |
|
3-5 |
≤1 |
≤1 |
≤0.07 |
≤0.4 |
Nb:0.15-0.45 |
8-13 |
| 304L |
18-20 |
8-12 |
|
|
≤2 |
≤1 |
≤0.03 |
≤0.4 |
|
9-12 |
| 410 |
11.5-14.5 |
|
|
|
≤1 |
≤0.6 |
≤0.15 |
≤0.4 |
|
9-12 |
| 420 |
12-14 |
≤0.6 |
≤0.65 |
|
≤1 |
≤0.6 |
0.16-0.25 |
≤0.4 |
|
9-12 |
| 420-A |
12-14 |
≤0.6 |
≤0.65 |
|
≤1 |
≤0.6 |
0.5-0.7 |
≤0.4 |
Nb:1-2 |
9-12 |
| 2507 |
24-26 |
6-8 |
3-5 |
|
≤1.2 |
≤0.8 |
≤0.03 |
≤0.4 |
|
9-12 |
| 430 |
16-18 |
≤0.6 |
|
|
≤1 |
≤0.8 |
≤0.12 |
≤0.4 |
|
9-12 |
| 440C |
16-18 |
≤0.6 |
≤0.75 |
|
≤1 |
≤0.8 |
1.3-1.6 |
≤0.4 |
|
9-12 |
| Cr12MoV(SKD11) |
11-12.5 |
|
0.4-0.6 |
|
≤0.4 |
≤0.4 |
1.45- 1.7 |
≤0.4 |
|
9-12 |
| FeCo50 |
|
|
|
|
|
|
≤0.1 |
≤0.4 |
Co:48-52 |
9-12 |
| F75 |
26-30 |
|
5-7 |
|
|
|
≤0.2 |
≤0.1 |
|
9-12 |
| FeSiCr |
5-6 |
|
|
|
|
5-6 |
|
|
|
- |
| 8620 |
0.4-0.6 |
0.4-0.7 |
0.15-0.25 |
|
|
|
0.12-0.23 |
|
|
4-8 |
2、气雾化 MIM不锈钢系列
| 牌号 |
成分 (Wt%) |
D50 |
| Cr |
Ni |
Mo |
Cu |
Mn |
Si |
C |
O |
Other |
| Q316L |
16-18 |
10-14 |
2-3 |
|
≤2 |
≤1 |
≤0.03 |
≤0.15 |
|
12.0-15.0 |
| Q17-4PH |
15.5-17.5 |
3-5 |
|
3-5 |
≤1 |
≤1 |
≤0.07 |
≤0.15 |
Nb:0.15-0.45 |
11.0-14.0 |
| Q304L |
18-20 |
8-12 |
|
|
≤2 |
≤1 |
≤0.03 |
≤0.15 |
|
11-14 |
| Q420 |
12-14 |
≤0.6 |
≤0.65 |
|
≤1 |
≤0.6 |
0.16-0.25 |
- |
|
11-14 |
| QM2 |
3.8-4.4 |
≤0.3 |
4.5-5.5 |
≤0.25 |
0.15-0.4 |
0.2-0.45 |
0.8-0.9 |
- |
V:1.75-2.2
W：5.5-6.75 |
- |
QFeSi系列
| ag真人国际官网 Products |
磁饱和感应强度Bmax |
磁损Core Loss |
居里温度Curie Temperature |
直流偏置DC-Bias |
| QFeSi |
16000Gs |
≤520mW/cm3@ue=60 |
700℃ |
≥75% @100 Oe |
| QFeSiAl |
10500Gs |
≤200mW/cm3@ue=60 |
600℃ |
≥60% @100 Oe |